PC沙伯基础（原GE）Resin EXL1414耐低温-40℃ 抗紫外线（***原版物性）
| TYPICAL PROPERTIES(1) | ||||
MECHANICAL | Value | Unit | Standard | |
Tensile Stress, yld, Type I, 50 mm/min | 560 | kgf/cm2 | ASTM D 638 | |
Tensile Stress, brk, Type I, 50 mm/min | 510 | kgf/cm2 | ASTM D 638 | |
Tensile Strain, yld, Type I, 50 mm/min | 6 | % | ASTM D 638 | |
Tensile Strain, brk, Type I, 50 mm/min | 98 | % | ASTM D 638 | |
Tensile Modulus, 50 mm/min | 20500 | kgf/cm2 | ASTM D 638 | |
Flexural Stress, yld, 1.3 mm/min, 50 mm span | 940 | kgf/cm2 | ASTM D 790 | |
Flexural Modulus, 1.3 mm/min, 50 mm span | 22700 | kgf/cm2 | ASTM D 790 | |
Hardness, Rockwell L | 89 | - | ASTM D 785 | |
Hardness, Rockwell R | 121 | - | ASTM D 785 | |
Tensile Stress, yield, 50 mm/min | 57 | MPa | *** 527 | |
Tensile Stress, break, 50 mm/min | 60 | MPa | *** 527 | |
Tensile Strain, yield, 50 mm/min | 6 | % | *** 527 | |
Tensile Strain, break, 50 mm/min | 120 | % | *** 527 | |
Tensile Modulus, 1 mm/min | 2150 | MPa | *** 527 | |
Flexural Stress, yield, 2 mm/min | 85 | MPa | *** 178 | |
Flexural Modulus, 2 mm/min | 2250 | MPa | *** 178 | |
IMPACT | Value | Unit | Standard | |
Izod Impact, notched, 23°C | 88 | cm-kgf/cm | ASTM D 256 | |
Izod Impact, notched, -30°C | 78 | cm-kgf/cm | ASTM D 256 | |
Instrumented Impact Total Energy, 23°C | 714 | cm-kgf | ASTM D 3763 | |
Izod Impact, unnotched 80*10*3 +23°C | NB | kJ/m2 | *** 180/1U | |
Izod Impact, unnotched 80*10*3 -30°C | NB | kJ/m2 | *** 180/1U | |
Izod Impact, notched 80*10*3 +23°C | 70 | kJ/m2 | *** 180/1A | |
Izod Impact, notched 80*10*3 -30°C | 60 | kJ/m2 | *** 180/1A | |
Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm | 70 | kJ/m2 | *** 179/1eA | |
Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm | 65 | kJ/m2 | *** 179/1eA | |
Charpy 23°C, Unnotch Edgew 80*10*3 sp=62mm | NB | kJ/m2 | *** 179/1eU | |
Charpy -30°C, Unnotch Edgew 80*10*3 sp=62mm | NB | kJ/m2 | *** 179/1eU | |
THERMAL | Value | Unit | Standard | |
Vicat Softening Temp, Rate B/50 | 145 | °C | ASTM D 1525 | |
HDT, 0.45 MPa, 3.2 mm, unannealed | 139 | °C | ASTM D 648 | |
HDT, 1.82 MPa, 3.2mm, unannealed | 124 | °C | ASTM D 648 | |
CTE, -40°C to 40°C, flow | 6.96E-05 | 1/°C | ASTM E 831 | |
CTE, -40°C to 40°C, xflow | 7.47E-05 | 1/°C | ASTM E 831 | |
CTE, 23°C to 80°C, flow | 7.2E-05 | 1/°C | *** 11359-2 | |
CTE, 23°C to 80°C, xflow | 7.2E-05 | 1/°C | *** 11359-2 | |
Ball Pressure Test, 125°C +/- 2°C | Passes | - | IEC 60695-10-2 | |
Vicat Softening Temp, Rate B/50 | 145 | °C | ***306 | |
Vicat Softening Temp, Rate B/120 | 146 | °C | ***306 | |
HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm | 140 | °C | *** 75/Be | |
HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 128 | °C | *** 75/Ae | |
Relative Temp Index, Elec | 130 | °C | UL 746B | |
Relative Temp Index, Mech w/impact | 120 | °C | UL 746B | |
Relative Temp Index, Mech w/o impact | 125 | °C | UL 746B | |
PHYSICAL | Value | Unit | Standard | |
Specific Gravity | 1.18 | - | ASTM D 792 | |
Mold Shrinkage, flow, 3.2 mm (5) | 0.4 - 0.8 | % | SABIC Method | |
Mold Shrinkage, xflow, 3.2 mm (5) | 0.4 - 0.8 | % | SABIC Method | |
Melt Flow Rate,300°C/1.2 kgf | 10 | g/10 min | ASTM D 1238 | |
Density | 1.19 | g/cm3 | *** 1183 | |
Water Absorption, (23°C/sat) | 0.35 | % | *** 62 | |
Moisture Absorption (23°C / 50% RH) | 0.15 | % | *** 62 | |
Melt Volume Rate, MVR at300°C/1.2 kg | 9 | cm3/10 min | *** 1133 | |
ELECTRICAL | Value | Unit | Standard | |
Volume Resistivity | >1.E+15 | Ohm-cm | ASTM D 257 | |
Surface Resistivity | >1.E+15 | Ohm | ASTM D 257 | |
Dielectric Strength, in oil, 0.8 mm | 16.2 | kV/mm | ASTM D 149 | |
Relative Permittivity, 100 Hz | 2.68 | - | ASTM D 150 | |
Relative Permittivity, 1 MHz | 2.64 | - | ASTM D 150 | |
Dissipation Factor, 100 Hz | 0.0012 | - | ASTM D 150 | |
Dissipation Factor, 1 MHz | 0.0093 | - | ASTM D 150 | |
FLAME CHARACTERISTICS | Value | Unit | Standard | |
Glow Wire Flammability Index 850°C, passes at | 0.8 | mm | IEC 60695-2-12 | |
Glow Wire Flammability Index 960°C, passes at | 1 | mm | IEC 60695-2-12 | |
Glow Wire Ignitability Temperature, 1.0 mm | 875 | °C | IEC 60695-2-13 | |
Glow Wire Ignitability Temperature, 3.0 mm | 875 | °C | IEC 60695-2-13 | |
Oxygen Index (LOI) | 37 | % | *** 4589 | |
| Parameter | ||
Injection Molding | Value | Unit |
Drying Temperature | 120 | °C |
Drying Time | 3 - 4 | hrs |
Drying Time (Cumulative) | 48 | hrs |
Maximum Moisture Content | 0.02 | % |
Melt Temperature | 295 - 315 | °C |
Nozzle Temperature | 290 - 310 | °C |
Front - Zone 3 Temperature | 295 - 315 | °C |
Middle - Zone 2 Temperature | 280 -305 | °C |
Rear - Zone 1 Temperature | 215 - 295 | °C |
Mold Temperature | 70 - 95 | °C |
Back Pressure | 0.3 - 0.7 | MPa |
Screw Speed | 40 - 70 | rpm |
Shot to Cylinder Size | 40 - 60 | % |
Vent Depth | 0.025 - 0.076 | mm |